鈣穩(wěn)定氧化鋯-定徑水口耐火材料
鈣穩(wěn)定氧化鋯空心球、顆粒和粉末是鋯基定型耐火材料的優(yōu)質原料。它是一種經(jīng)過氧化鈣 (CaO) 化學穩(wěn)定的電熔氧化鋯。鈣穩(wěn)定氧化鋯在高溫下能夠保持其立方晶體結構。因此，其熱性能更佳，尤其具有高抗腐蝕性和抗熱震性。它可以防止定型耐火材料開裂。
Calcia-Stabilized Zirconia grain is a superior raw material for zirconium base shaped refractories. It is a type of fused zirconia that has been chemically stabilized with calcium oxide (CaO). Calcia stabilized zirconia can maintain its cubic crystal structure at high temperature. Thus the thermal performance is better especially with high anti-corrosion, and thermal shock resistance. It can avoid the shaped refractories cracking.
特性：
1. 高熔點（約2700°C）。
2. 良好的抗熱震性。
3. 中等離子電導率。
4. 化學惰性和耐腐蝕性。
5. 與釔穩(wěn)定氧化鋯相比，成本效益更高。
Properties:
1. High melting point (~2700°C).
2. Good thermal shock resistance.
3. Moderate ionic conductivity.
4. Chemical inertness & corrosion resistance.
5. High cost effective compared to Yttrium stabilized zirconia.
鈣穩(wěn)定氧化鋯的化學成分 (%)：
成分Item | 空心球Bubble | 3%CSZ顆粒(3% CSZ Grain) | 7%CSZ顆粒(7% CSZ Grain) |
ZrO2 | Min. 95 | Min. 94 | Min. 91 |
CaO | 3.0-4.0 | 3.0-4.5 | 7.0-7.8 |
SiO2 | Max.0.30 | Max.0.40 | Max.0.40 |
Al2O3 | Max.0.20 | Max.0.20 | Max.0.20 |
Fe2O3 | Max.0.05 | Max.0.10 | Max.0.10 |
TiO2 | Max.0.20 | Max.0.20 | Max.0.20 |
鈣穩(wěn)定氧化鋯的物理指標：
比重Specific Gravity | 5.6-5.9 g/cm3 |
熔點Melting point | 2700° |
硬度Hardness | 維氏硬度12.5 GPA |
穩(wěn)定化率Stabilization Rate | 70-95% |
常規(guī)型號Specification:
空心球Bubble | 0-1mm,1-3mm,3-5mm,5-8mm,1-5mm,等 |
顆粒&粉末 Grain & Powder | 50#,60#,80#,150#,200#,325#800#,1000#,1500r,2000#, 2500#,3000#,4000#,6000#,8000# 等 |
l 其他型號的空心球、顆粒、粉末可定制。Customized bubble & grain & powder are available upon request.
鈣穩(wěn)定氧化鋯的用途：
1. 煉鋼爐定徑水口、滑動水口、浸入式長水口。
2. 鋯基輕質耐火磚及定型耐火材料。
3. 高品質窯具。
4. 電子陶瓷，如承燒板和匣缽。
5. 磨料行業(yè)及耐磨添加劑，如汽車剎車片。
Calcia Stabilized Zirconia Application：
1. Fixed diameter nozzle plug, sliding gate, immersion water plug in steel making furnace.
2. Zirconia base lightweight fire bricks and shaped refractories.
3. High quality kiln furniture.
4. Electronic ceramics such as setter plates and saggers.
5. Abrasive industry and wear resistance additives such as auto brake lining.